Rosalia Pink |
|
|
| |
|
|
|
|
| Rosalia Pink |
| Physical, mechanical and technological specifications : |
| Hardness |
(Mohs) |
: |
3-4 |
| Unit Volume Weight |
(gr/cm3) |
: |
2,67 |
| Density |
(gr/cm3) |
: |
2,68 |
| Water absorption at atmospheric pressure |
by weight (%) |
: |
0,26 |
| |
by volume (%) |
: |
0,69 |
| Water absorption at boiling water |
by weight (%) |
: |
0,21 |
| |
by volume (%) |
: |
0,56 |
| Porosity |
(%) |
: |
0,69 |
| Compressive strength |
(Kg/cm2) |
: |
841,06 |
| Compressive strength after freezing |
(Kg/cm2) |
: |
840,14 |
| Strength to blow |
(Kg/cm2) |
: |
4 |
| Strength to bending |
(Kg/cm2) |
: |
144,19 |
| Modulus of Elasticity |
(Kg/cm2) |
: |
72x2x10³ |
| Ratio of fullness |
(%) |
: |
99,63 |
| Degree of pores |
(%) |
: |
0,37 |
| Average Abrasion Loss |
(cm3/50 cm2) |
: |
3,1 |
| Average Tensile Strength |
(Kg/cm2) |
: |
42 |
| |
| Chemical analysis |
|
|
|
| CaO.................................................................................................... |
55,02 |
| MgO.................................................................................................... |
0,34 |
| SiO2.................................................................................................... |
2,08 |
| A12O3................................................................................................. |
0,40 |
| Fe2O3................................................................................................. |
2,69 |
|
|
|
|
| |
|
|
| |
|
|
|
|
|
|